01-28-2007, 12:37 AM
Quote:Interesting thoughts Mike. The parallels are obvious when you compare the item you describe. Do you have any pictures of it?
The drawing in the catalogue was not mine so I can't post it here.
Quote:I would find it unusual though that a fan handle would be made of a solid cast copper alloy. Bone seems much more applicable when you consider its uses. This has quite some weight to it, and as you mentioned the example you speak of is quite longer.
All sort of implements were made out of cast copper alloy and it would be quite normal to find an object like a fan handle made this way. The length is neither here nor there as designs may have varied.
Quote:What about a later period helmet? Not being bronze like the Montefortino or Coolus. Many of them still had a copper alloy knob on top. I can't see them welding one of those to Iron. How were they mounted then? Could they not have been riveted to a Bronze cross brace?
No, there are no parallels I am aware of attached to or associated with helmets. I'm afraid wanting it to be a crest knob doesn't make it so; still, it's an interesting object and I shall get Lindsay Allason-Jones to have a look at the piccies as she's much better at the non-military stuff than me. If a fan handle, it's a darned sight rarer than a crest knob!
Solder was occasionally used on ferrous metal objects, but I don't think you can weld/braze iron/steel and any of the copper alloys together because of the melting points (but some of the metal bashers will give you a better answer on that than me). I have little doubt that if the Romans had had Blu-Tak or double-sided tape they'd have used that!
Mike Bishop