11-18-2013, 01:07 AM
No need to worry then,you didn't get to a temp that will cause you any problems.
The first time I heat treated a long blade it warped a little and,even though I knew better I instinctively reached up and tried to *true* it up right out of the quench... ended up with a dagger and about 8 arrow heads :grin:
On the leather,to be honest I still am not sure... unless it is undeyed tooling leather I have a hard time spotting what is what, sorry.
The first time I heat treated a long blade it warped a little and,even though I knew better I instinctively reached up and tried to *true* it up right out of the quench... ended up with a dagger and about 8 arrow heads :grin:
On the leather,to be honest I still am not sure... unless it is undeyed tooling leather I have a hard time spotting what is what, sorry.
Dave Akers http://davesons.webs.com/